Calculating the Lattice Mismatch of GaN/Sapphire 
Share this thread: 
#1
May2714, 09:23 PM

P: 12

Dear Physics Forum
It has been reported that the lattice mismatch of GaN/Sapphire is ~13.9%. I have tried the following formula, but got the wrong answer: [(GaNAl2O3)/GaN] x 100% where: GaN = 3.189 Angstroms Al2O3 = 4.765 Angstroms Obviously I am missing something huge. Thank you. 


#2
May2814, 04:29 AM

Sci Advisor
P: 1,627

In crystal growth things depend strongly on things like crystal orientation, which surface you choose, crystal growth direction, inplane orientation and such stuff. So you need to know which planes you are talking about. 13.8% is what you get if you use the (1010) and (1120) planes of GaN and sapphire.
See: http://www.icdd.com/resources/axa/vol43/v43_047.pdf 


#3
May2814, 07:13 AM

Sci Advisor
PF Gold
P: 2,241

Just to add to what was said above: Sappbhire is extremely anisotropic meaning there are many ways you can cut it to make a substrate.
The most common type of substrate used is Rcut; which is actually cut at an "angle" with respect to the "zaxis"(note that you actually need four indices to define a plane in sapphire). You can also buy for example ccut and rcut (note that R and r are different cuts) Note that this "flexibility" is one reason why sapphire is so popular, you can make it "fit" to a large number of other materials by just using the right cut. 


#4
May2814, 10:37 PM

P: 12

Calculating the Lattice Mismatch of GaN/Sapphire
I have calculated this using the same formula and have arrived at a value of 14%, which should be tolerable since my database and C. J. Rawn's would exhibit different degree of strain. The interplanar spacing for GaN(1010) and Al2O3(1120) is 2.762 angstroms and 2.375 angstroms, respectively. So, one can't just choose to use the length of a unit cell to calculate the lattice mismatch. The plane relationship must be determined first. Thank you again. Anyway, below is an image of how (I think) the hexagonal cells are arranged. ps: most papers also report that the GaN has no problem aligning its caxis along with the substrate's, but the aaxis (and therefore, baxis) will usually twist 60 degree with respect to the substrate. 


#5
May2814, 10:42 PM

P: 12

I did not realise that rcut and Rcut are prepared with a different plane face. Some reports said that they used sapphire (1102) for their substrates. Now I am not sure if this is an r or Rsapphire. 


Register to reply 
Related Discussions  
Calculating lattice energy on ionic compound  Biology, Chemistry & Other Homework  1  
Lattice mismatch  Atomic, Solid State, Comp. Physics  0  
Calculating lattice enthalpy of FeF2  Biology, Chemistry & Other Homework  1  
Calculating the interplanar distance d111 for an FCC lattice  Advanced Physics Homework  1  
Q: Calculating gravitation inside a lattice  General Physics  0 