more rust in less salt??
As part of my chemistry experiments on corrosion, I am noticing that the steel nails are rusting more in solutions of 3.5g/L salt, than 35g/L salt. What could be some reasons to explain this??
I would have thought that the 35g/L solutions would have lead to more rust, not less.
Perhaps there is another reaction going on.