Carbon Content decrease after Cold-forging process?

soo33y

Hi guys,

I've come across an abnormality at work with regards to Carbon Content.

The raw material used was 1010 CHQ which should have a carbon content of 0.08 - 0.13.

However after going through a cold-forging process, we tested the final product and found that the Carbon Content decreased to 0.041.

How did this happen? Is it possible? Can someone explain?

Really stumped at this stage.

Cheers,
Daniel.

Enthalpy

No explanation. That sounds astounding to me.

Maybe there was some segregation and the tiny place where you measured was chosen unluckily?

pukb

segregation may lead to C atoms migrating to surface of the material.
But this should not be a problem unless the material is heated for a long time.
If heated for a long time and tested after heating inside the material, the result of yours seems to be acceptable.

Similar discussions for: Carbon Content decrease after Cold-forging process?
Thread	Forum	Replies
Heating Requirements for Forging Process	Engineering Systems & Design	0
The carbon content of a good samari sword	Chemistry	3
carbon content in steel and corrosion	Biology, Chemistry & Other Homework	1
Effect of Carbon Content in Steel	Biology, Chemistry & Other Homework	2
Effect of Mn content in medium Carbon steel	Materials & Chemical Engineering	0

Enthalpy	No explanation. That sounds astounding to me. Maybe there was some segregation and the tiny place where you measured was chosen unluckily?

pukb	segregation may lead to C atoms migrating to surface of the material. But this should not be a problem unless the material is heated for a long time. If heated for a long time and tested after heating inside the material, the result of yours seems to be acceptable.