Difficulty in electroetching of 1050 aluminum alloy

by materials
Tags: 1050, alloy, aluminum, difficulty, electroetching
Share this thread:
materials
#1
Jan22-14, 07:19 AM
P: 2
Dear friends
I have tried to electroetch 1050 aluminum alloy by 5ml phosphoric acid + 95ml H2o under 1 to 10 volts. However, it was a complete failure even after etching for 6 min.

Please help me if you know how to overcome this problem.

Thank you very much
Best regards
Phys.Org News Partner Engineering news on Phys.org
Comfortable climate indoors with porous glass
Crash-testing rivets
Customized surface inspection
Lok
#2
Jan28-14, 05:13 AM
P: 442
What does failure mean?
All you wish to do is electroetching aluminum?
Why not NaOH http://www.youtube.com/watch?v=E5QXOynT-Fs
Is the oxide layer thin? I usually get at least electrolysis and some etching with tap water. Are any bubbles coming out?
Are you sure you used the right polarity?

A few startup questions.


Register to reply

Related Discussions
Friction during extrusion of Aluminum alloy Mechanical Engineering 0
Aluminum Alloy Fatigue Information General Engineering 6
Aluminum alloy Grains, Which alloy is it? Materials & Chemical Engineering 1
Corrosion of aluminum alloy 319.0 help Materials & Chemical Engineering 3
Heat Treatment of Aluminum Alloy Chemistry 0