Difficulty in electroetching of 1050 aluminum alloy


by materials
Tags: 1050, alloy, aluminum, difficulty, electroetching
materials
materials is offline
#1
Jan22-14, 07:19 AM
P: 2
Dear friends
I have tried to electroetch 1050 aluminum alloy by 5ml phosphoric acid + 95ml H2o under 1 to 10 volts. However, it was a complete failure even after etching for 6 min.

Please help me if you know how to overcome this problem.

Thank you very much
Best regards
Phys.Org News Partner Engineering news on Phys.org
Fiber-optic microscope will help physicians detect cancer, diseases at early stages
Wind tunnel tests support improved aerodynamic design of B61-12 bomb
Smart sensor technology to combat indoor air pollution
Lok
Lok is offline
#2
Jan28-14, 05:13 AM
P: 406
What does failure mean?
All you wish to do is electroetching aluminum?
Why not NaOH http://www.youtube.com/watch?v=E5QXOynT-Fs
Is the oxide layer thin? I usually get at least electrolysis and some etching with tap water. Are any bubbles coming out?
Are you sure you used the right polarity?

A few startup questions.


Register to reply

Related Discussions
friction during extrusion of Aluminum alloy Mechanical Engineering 0
Aluminum Alloy Fatigue Information General Engineering 6
Aluminum alloy Grains, Which alloy is it? Materials & Chemical Engineering 1
Corrosion of aluminum alloy 319.0 help Materials & Chemical Engineering 3
Heat Treatment of Aluminum Alloy Chemistry 0