Pickling of steel in Hydrochloric Acid

by selseg
Tags: acid, hydrochloric, pickling, steel
Share this thread:
selseg
#1
Apr9-14, 03:13 PM
P: 27
I have some pieces of rusted mild steel pipes that i intend to remove rust from.I inserted a test sample in 15% Hydrochloric acid for 4 hours after which all the rust was removed from the surface and corrosion has slowed dramatically after washing off the acid.The subsequent pieces of steel pipe I tried on a large scale showed rapid corrosion soon after the pipes have been removed from the acid .What could be the cause of this
Phys.Org News Partner Engineering news on Phys.org
New filter technology uses inert gas to bore holes in high-quality steel
Augmented reality helps in industrial troubleshooting
How wireless technology can dramatically improve ship safety
Baluncore
#2
Apr20-14, 02:18 AM
Sci Advisor
Thanks
P: 1,910
Chlorine from the HCl remains on the steel surface and causes corrosion to return. Once an iron surface is poisoned with chlorine it is close to impossible to remove. It is a real problem in marine situations and causes car bodies to rust where salt is used on the road to prevent ice.

A slower process, that is often preferred by tool and machinery re-builders, is to immerse a rusty item in molasses for a week.
http://www.practicalmachinist.com/vb...olasses-90452/

There are commercial rust converters that protect the surface with a phosphate.


Register to reply

Related Discussions
Phosphoric acid vs. Hydrochloric acid when removing rust and rerusting Biology, Chemistry & Other Homework 5
What vessels to use with hydrochloric acid, sodium hydroxide, and sulfuric acid? Chemistry 1
Acid-Base Titrations - Soda Lime and Hydrochloric Acid Biology, Chemistry & Other Homework 7
Hydrochloric acid solution is needed to make 31 g boric acid? Chemistry 6
Hydrochloric Acid Chemistry 1