Annealing of aggregated nanoparticles (in solution)

Share this thread:
JeroenV
#1
May2-12, 10:20 AM
P: 2
If you have a colloid of 2 types of nanoparticles and tune the conditions (pH, salt) in such a way that one of the two particles aggregates to the surface of the other (opposite zeta potential), would it then be possible to thermally anneal this system? The end goal would be that the 2 types of nanoparticles are attached to eachother and do not need opposite surface charge anymore to stay attached. Is this possible?
Phys.Org News Partner Engineering news on Phys.org
ESA investigates an alternative, environmental-friendly method of corrosion resistance
The oscillator that could makeover the mechanical watch
Engineers study bats to improve aviation travel
siddharth
#2
May2-12, 02:03 PM
HW Helper
PF Gold
siddharth's Avatar
P: 1,197
I expect the nanoparticle aggregate will simply precipitate out of solution when you mix them together if you use the same solution. If you're trying to structure a multi-layer of nanoparticles though, that can be done using the Layer-by-Layer technique, if you sequentially dip a substrate into oppositely charged nanoparticle solutions so you can essentially build up layers of these particles. See this paper, for an example of how the LbL technique can be used to do this: http://pubs.acs.org/doi/abs/10.1021/la701267a
JeroenV
#3
May4-12, 04:45 AM
P: 2
Thank you for your answer. By tuning the concentrations, LbL can be used without forming to big aggergates. However, my concern was if it is possible to thermally anneal the multi-layered particle after LbL. In this case they are physically attached (crystal structures are combined, however with surface defects). Then, the you can go ahead and change the pH without losing your multi-layered structure.


Register to reply

Related Discussions
Effect of annealing temperature on Capacitance of MOS-C Introductory Physics Homework 0
Standard deviation of aggregated data Set Theory, Logic, Probability, Statistics 3
Structural Difference in Annealing vs Untreated Steel Materials & Chemical Engineering 1
Annealing effect on PL efficiency Atomic, Solid State, Comp. Physics 2
Annealing before and after pellet formation Atomic, Solid State, Comp. Physics 3