Equilibrium for diffusion of gases in metals

by hannaha
Tags: diffusion, equilibrium, gases, metals
hannaha is offline
Jan7-13, 05:10 PM
P: 1
Hi there,

This could be absolute nonsense but I just got thinking about this. Say you had a certain metal into which a quantity of hydrogen had diffused, and then you placed it in communication with another hydrogen-free metal (say, titanium), would it be possible that the hydrogen would move into the titanium metal, out of the other metal? Coming from a a biology background I was thinking about osmosis (well, any concentration gradient-type process) - does the same apply to gases in metals i.e. would an equilibrium be reached? Or is there no driving force created by the "empty" metal?

Any ideas would be appreciated, thanks!
Phys.Org News Partner Engineering news on Phys.org
SensaBubble: It's a bubble, but not as we know it (w/ video)
WSU innovation improves drowsy driver detection
Faster computation of electromagnetic interference on an electronic circuit board
Enthalpy is offline
Jan8-13, 07:22 AM
P: 660
I understand it just as you suggest, and this is backed by diffusion processes in semiconductors. Not just for hydrogen, but as well for dopants.

You need an excellent contact between the solids so (1) the diffusing species don't need to pass through air in between (2) hydrogen doesn't go away through the slit.

Also interesting: solids have some affinity for the diffusing species, so the equilibrium between contacting solids is not at identical concentrations.
chill_factor is offline
Jan9-13, 02:01 PM
P: 887
there is a driving force indeed. there is a driving force even for a hydrogen permeated metal in empty space. its just the kinetics that's a problem.

if you weld 2 alloys together, even the alloys start diffusing into one another; however, it may be extremely slow.

mzain is offline
Jan18-13, 12:29 PM
P: 4

Equilibrium for diffusion of gases in metals

there are certain conditions that needs to be fulfilled for a specific reaction to occur. for example for titanium and hydrogen the start of reaction takes place at 300 C. and for the reaction to occur the there must be a contact between the metals in your case. and it will be diffusion controlled process.

i hope it will help u to some extent

Register to reply

Related Discussions
slater orbitals for alkali earth metals and noble gases Chemistry 9
Diffusion Coefficient for gases at different temperatures Classical Physics 1
hw help diffusion of gases Biology, Chemistry & Other Homework 4
Diffusion of Different Gases/Particles through Air General Physics 0
Helium diffusion through metals Classical Physics 1