Did a Shear-Tensile Failure Cause the Wire Rope Accident?

  • Thread starter Thread starter zerodish
  • Start date Start date
  • Tags Tags
    Failure Tensile
AI Thread Summary
The discussion centers on a wire rope accident involving a 7-strand aluminum wire that caused automobile accidents after tangling with utility poles. Observers note that the wire appears to have sheared diagonally, suggesting it did not fail under tension, as a tensile failure would typically show ragged ends or thinning. Factors such as wear against abrasive surfaces, swinging in the wind, and potential damage from being driven over are considered as possible causes of the shearing. The complexities of the cable's configuration and external loads complicate the analysis of the failure. Overall, the exact events leading to the wire's failure remain unclear, highlighting the need for further investigation.
zerodish
Messages
11
Reaction score
1
I have been photographing wires hanging from utility poles that have tangled with and caused automobile accidents. One of these is a puzzle the detail shows a wire from a 7 strand wire rope made out of aluminum. It was too dangerous at the time to anything but drag the wire out of the road and the wire has been removed by the utility. http://www.flickr.com/photos/78934859@N04/12562669533/in/photolist-k97XYz-cabvfq-euZ4FC-hEtawu
 
Engineering news on Phys.org
Can't you just upload the pic here ? to view the pic one needs to sign up for flickr...
 
Last edited by a moderator:
The wire appears to have been sheared diagonally.
If it had failed under tension I would expect a ragged end or a thinning.

It is possible that it was worn over time against an abrasive surface.
Maybe swinging or vibrating in the wind.
 
Here is the photo you can view it on flickr by searching "national electrical code" in quotes.
 

Attachments

  • P2160324.JPG
    P2160324.JPG
    71.2 KB · Views: 473
Definitely not tensile failure. I concur with Baluncore. You would see a thinning of the material at the point of break. Possibly broken when it was driven over and dragged along the roadway.
 
It's really tough to say...
(1) these cables are wrapped in a 7 cable bundle, most often twisted to maintain shape.
(2) Power cables are in tension but they are catenaries, this, coupled with (1) could cause some very odd shearing action, especially coupled with other loads (wind, entanglement, etc)

There's not much thinning in shear-tensile failures in wire rope. That's a really long "shear plane" (if that's what it is) though...

These factors make it difficult to tell what had happened. Do you know the events which led up to this failure?
 
Thread 'Physics of Stretch: What pressure does a band apply on a cylinder?'

Thread 'Physics of Stretch: What pressure does a band apply on a cylinder?'

Scenario 1 (figure 1) A continuous loop of elastic material is stretched around two metal bars. The top bar is attached to a load cell that reads force. The lower bar can be moved downwards to stretch the elastic material. The lower bar is moved downwards until the two bars are 1190mm apart, stretching the elastic material. The bars are 5mm thick, so the total internal loop length is 1200mm (1190mm + 5mm + 5mm). At this level of stretch, the load cell reads 45N tensile force. Key numbers...
View full post »

Thread 'Cantilever help'

I'm trying to decide what size and type of galvanized steel I need for 2 cantilever extensions. The cantilever is 5 ft. The space between the two cantilever arms is a 17 ft Gap the center 7 ft of the 17 ft Gap we'll need to Bear approximately 17,000 lb spread evenly from the front of the cantilever to the back of the cantilever over 5 ft. I will put support beams across these cantilever arms to support the load evenly
View full post »

Similar threads

How bright is the future of Maglev Cars?
Replies
19
Views
11K
Mathematica This Week's Finds in Mathematical Physics (Week 228)
Replies
2
Views
3K
Mathematica This Week's Finds in Mathematical Physics (Week 228)
Replies
2
Views
4K

Hot Threads

Recent Insights

Back
Top