How to calculate the carrier concentration

myousuf
Messages
4
Reaction score
0
Can any please help me in solving the following two questions

Q1
A Si sample is doped with 10^16 per cm cube boron atoms and a certain
number of shallow donors. The fermi level (Ef) is 0.36 eV above Ei
(intrinsic energy level) at 300K. What is the donor concentration Nd?

For Si at 300K ni(intrinsic carrier concentration) = 1.5 x 10^10 per
cm cube




Q2
A Si sample contains 10^16 per cm cube In(indium) acceptor atoms and
a certain number of shallow donors. The In (indium) acceptor level is
0.16 eV above Ev(Valence band edge), and Ef is 0.26eV above Ev at
300K. How many in atoms in cm per cube are unionized (i.e. neutral)?

For Si at 300K ni(intrinsic carrier concentration) = 1.5 x 10^10 per
cm cube




There is no additional information available. Please state the
question number when answering and indicate any formulas used.

The following equations may prove useful

n(o) x p(o) = ni^2

n(o) = ni x e((Ef-Ei))/KT)

p(o) = ni x e((Ei-Ef)/KT)
 
Last edited:
Physics news on Phys.org
What have you done so far? If you want help, than you should say what you think and what you have tried.

Is there any more relations that you know of? How about "carge neutralisty condition of doped semi conductor" ? And Law of mass action?
 
This is what I have came up with so far for question number 1

using the relation n(o) = ni x e((Ef-Ei))/KT)

with Ef-Ei=0.36 x 1.6 x 10^-19 , ni=1.5 x 10^10, T=300k , K=1.38 x 10^-23

we get n(o) = 1.654 x 10^16 per cm cube

However there are 10^16 B atoms to neutralize these charges

Hence Nd = 1.654 x 10^16 - 10^16 = 6.5 x 10^15 per cm cube
 
For question number 2

unionized atoms are left at the acceptor level

Ef-Ev=0.26eV

Ea-Ev=0.16eV

Ea-Ef=0.16-0.26= -0.10eV

Using fermi-driac statistics f(E)=1/(1+e((E-Ef)/KT)))

for E=Ea,T=300 and substituting all the constants

f(E)=1/(1+e((Ea-Ef)/KT))), gives = 0.9794

However fermi driac statistics give the probablity of occupance of an electron in an Energy state E. hence 0.9794 is the probablity of occupance of an electron.

hole probablity of occupance=1-electron probablity of occupancy

hole probablity of occupance of the energy state Ea = 1-0.9794 = 0.02053

unionized atoms are left at the acceptor level(Ea)

Hence, number of IN(indium) atoms left unionized = hole probabilty of occupancy of Energy state Ea x number of In acceptor atoms

=0.02053 x 10^16

=2.05 x 10^14
 
Anyway there are still questions that remain unanswered

For instance, what role does shallow donor impurities have to play in question number 2.

Any suggestions to the proposed solution above will be highly appreciated
 
Last edited:
To solve this, I first used the units to work out that a= m* a/m, i.e. t=z/λ. This would allow you to determine the time duration within an interval section by section and then add this to the previous ones to obtain the age of the respective layer. However, this would require a constant thickness per year for each interval. However, since this is most likely not the case, my next consideration was that the age must be the integral of a 1/λ(z) function, which I cannot model.