How to quantify knife-edge sharpness

  • Thread starter Thread starter mooktank
  • Start date Start date
AI Thread Summary
Quantifying knife-edge sharpness remains a challenge, as sharpness is subjective and difficult to measure precisely. The discussion suggests grinding the edge until a burr forms and then removing it, as this indicates optimal sharpness. The participants emphasize the importance of creating a prototype to evaluate how well the blade retains its sharpness over time. The blade in question is made from CPM-S90V steel, known for its quality in knife-making. Ultimately, clear communication with the machine shop about the burr removal process is essential for achieving the desired edge quality.
mooktank
Messages
41
Reaction score
1
I'm designing a cutting blade and I'm working on the drawing right now. I have the geometry and surface finish spec'd but I was wondering is there some way to quantify sharpness of an edge? Can I just say to grind the edge until a burr forms and knock the burr off?
 
Engineering news on Phys.org
I believe I've heard of this before. The best steel blades are melted and folded... melted and folded--- look at the samurai blade.

What you said sounds right, just make sure have some sort of edge to begin with. I think I the actually cut the burr off with another knife if I remember correctly.
 
Sharpness I don't think can be quantified. However, you might would want make a prototype and check how well it holds it's sharpness--- that is the true test.
 
violin_writer said:
Sharpness I don't think can be quantified. However, you might would want make a prototype and check how well it holds it's sharpness--- that is the true test.

We're making the blade from CPM-S90V, a particle metallurgy steel. It makes a very good blade and we've done some testing with a blade that's not as sharp as it could be.

I just want the machine shop to be able to make the part properly.
 
cool...

I think you just tell them to knock the burr off, because when a blade has a burr it's as sharp as it can get. At least that what I saw in "how it's made" or a show like it with kitchen knives.
 
I need some assistance with calculating hp requirements for moving a load. - The 4000lb load is resting on ball bearing rails so friction is effectively zero and will be covered by my added power contingencies. Load: 4000lbs Distance to travel: 10 meters. Time to Travel: 7.5 seconds Need to accelerate the load from a stop to a nominal speed then decelerate coming to a stop. My power delivery method will be a gearmotor driving a gear rack. - I suspect the pinion gear to be about 3-4in in...
How did you find PF?: Via Google search Hi, I have a vessel I 3D printed to investigate single bubble rise. The vessel has a 4 mm gap separated by acrylic panels. This is essentially my viewing chamber where I can record the bubble motion. The vessel is open to atmosphere. The bubble generation mechanism is composed of a syringe pump and glass capillary tube (Internal Diameter of 0.45 mm). I connect a 1/4” air line hose from the syringe to the capillary The bubble is formed at the tip...
Thread 'Turbocharging carbureted petrol 2 stroke engines'
Hi everyone, online I ve seen some images about 2 stroke carbureted turbo (motorcycle derivation engine). Now.. In the past in this forum some members spoke about turbocharging 2 stroke but not in sufficient detail. The intake and the exhaust are open at the same time and there are no valves like a 4 stroke. But if you search online you can find carbureted 2stroke turbo sled or the Am6 turbo. The question is: Is really possible turbocharge a 2 stroke carburated(NOT EFI)petrol engine and...
Back
Top